Introduction

Compared with micron-sized graphene oxide (GO), nano-sized GO, especially graphene quantum dots (GQDs), exhibit superior physicochemical, optical, and photoelectric properties, e.g., biocompatibility, hydrophilicity, chemical stability, resistance to photo-bleaching and stable fluorescence (FL) emission, exhibiting great application potentials in bio-imaging, drug/gene delivery and photo-catalysis [1, 2]. So far, various carbon sources have been used to prepare GQDs, e.g., graphene, graphite, carbon nanotube, carbon fiber and active carbon, etc. [3, 4]. Nevertheless, those carbon-based precursors are relatively expensive, and hence it is imperious to discover an alternative precursor with abundant source and low cost for GQDs synthesis [4–6].

As an earth-abundant and low-cost fossil fuel, coal contains nano-sized sp² carbon areas, separated by sp³ amorphous carbons [5]. In 2013, GQDs were first synthesized by oxidation of coal using H₂SO₄ and HNO₃ (3:1) [4]. Using similar approaches, various blue GQDs and carbon quantum dots (CQDs) were then developed. For instance, by altering the reaction temperature (e.g., 50°–150°C) in strong acid, multicolor GQDs (from green to orange-red) were reported by Ye et al [5]. Alternatively, GQDs with adjustable colors can also be prepared via electrochemical exfoliation of coke [6]. More recently, H₂O₂ was used as a green oxidant to produce blue GQDs via hydrothermal treatment, where black carbon was selected as precursor [7]. Although electrochemical exfoliation and H₂O₂ treatment are promising approaches for the synthesis of GQDs in a greener way, it should be noted that those methods are only effective for certain kinds of coal [6, 7]. Hence, it is still a great challenge to develop a universal and effective approach for fabricating multicolor GQDs from low-cost coal. Furthermore, the size and structure effect of the GQDs (e.g., sp² carbon or sp³ carbon dominance) on cell viability is still poorly understood. In the current study, anthracite-derived multicolor GQDs (from blue to orange-red) were prepared via acid oxidation at different temperatures. The size and structure effect of the GQDs on cell viability was highlighted, while FL imaging in vitro using those GQDs was also tested.

Materials and methods

Results

The Raman and XRD spectra of anthracite were shown in Supplementary material, suggesting that anthracite contains a certain amount of sp² carbon areas. As shown in Figure 1, anthracite powders were first oxidized in strong acid at a certain temperature for 24 h, resulting in a clear brown solution. The resulted products are named as GQDs 100, GQDs 120, GQDs 130, and GQDs 150, respectively, depending on the reaction temperature. More details about GQDs synthesis and characterizations can be found in the Supplementary material. GQDs 100, GQDs 120, GQDs 130, and GQDs 150 solutions were found to be orange-red, yellow-green, green, and blue under 365 nm excitation UV (ultraviolet) lamp (Figure 1), respectively.

Display full size

Figure 1. 

Schematic diagram of preparing multicolor GQDs (solution of GQDs under 365 nm excitation UV lamp)

Nano-structure and size distribution of the GQDs 100, GQDs 120, GQDs 130, and GQDs 150 were studied using high resolution transmission electron microscopy (HRTEM) in Figure 2. GQDs 100 were found to be a mixture of large-sized amorphous CQDs (~50 nm) and smaller sized GQDs (~5 nm). The HRTEM image of GQDs shows a clear lattice spacing of ~0.21 nm, corresponding to the (102) lattice space of graphitic carbon. A mixture of amorphous CQDs (~30 nm) and GQDs (~3 nm) were also observed for the GQDs 120. The average sizes of the GQDs 130 and GQDs 150 were measured to be ~5 nm and ~2 nm, respectively. Amorphous CQDs were not found in the GQDs 130 and GQDs 150 samples, suggesting amorphous carbon in anthracite was completely oxidized under those conditions.

Display full size

Figure 2. 

HRTEM images and size distribution of the GQDs 100, GQDs 120, GQDs 130 and GQDs 150

As shown in Supplementary material, morphologies and height profiles of GQDs 100, GQDs 120, GQDs 130 and GQDs 150 were measured by atomic force microscope (AFM). GQDs 100 and GQDs 120 contain particles with various sizes, in good agreement with the transmission electron microscopy (TEM) observation in Figure 2. Height profiles of the GQDs 100 were found to be 4–10 nm, suggesting a mixture of 4–10 layers of GO. Thickness of the GQDs 120 were in the range of 1–4 nm, indicating 1–4 layers of GO. In comparison, size of the GQDs 130 and GQDs 150 were found to be more monodispersed, correlating well with the TEM data (Figure 2). Height profiles of the GQDs 130 and GQDs 150 were found to be ~1 nm, confirming a single layer of GO.

According to Figure 3A, all GQDs exhibited a strong UV absorption between 200–230 nm due to the π-π* electron transition of C=C bonds, while a shoulder between 300–350 nm was observed possibly attributed to the n-π* transformation of C=O bonds. Maximum emission peaks were found at 550 nm, 530 nm, 500 nm, and 440 nm when the GQDs 100, GQDs 120, GQDs 130, and GQDs 150 were stimulated at 470 nm, 470 nm, 430 nm, and 340 nm, respectively (Figure 3B–F). The GQDs size dependent blue shift of the emission wavelength should partially ascribed to the quantum confinement effect, considering the size difference among the GQDs [8]. Furthermore, all GQDs underwent a red shift on the FL emission with increasing excitation wavelength, which was commonly seen for GQDs, indicating an excitation-dependent behavior [9–11].

Display full size

Figure 3. 

Photoluminescence (PL) of the GQDs. A. Ultraviolet-visible (UV-Vis) absorption spectra of GQDs; B–E. FL emission spectra under different excitation waves for the GQDs 100, GQDs 120, GQDs 130, and GQDs 150, respectively; F. the maximum emission of GQDs showing blue-shift

The XPS spectra (Figure 4) showed that the GQDs are primarily consisted of C and O elements, including fractions of Csp² (284.5 eV), Csp³ (285.3 eV), C−O (287.2 eV), and COOH (289.2 eV) peaks [12]. Area fractions of the Csp² peaks were measured to be 4.1%, 12.5%, 46.1%, and 46.9% for the GQDs 100, GQDs 120, GQDs 130, and GQDs 150, respectively. Whereas the fractions of Csp³ peaks were reduced from 53.3% to 21.1% when increasing the reaction temperature from 100°C (GQDs 100) to 150°C (GQDs 150). The XPS data suggests high temperature intensifies oxidation of the amorphous sp³ carbon, resulting in GQDs with higher crystalline structure (Csp²), in good agreement with the HRTEM data in Figure 2.

Display full size

Figure 4. 

High-resolution C 1s XPS spectrum for the GQDs 100, GQDs 120, GQDs 130, and GQDs 150, respectively (XPS survey is inset). a.u.: absorbance unit

To explore the PL origin of GQDs, the time-resolved emission spectra (TRES) of the GQDs 100, GQDs 120, GQDs 130, and GQDs 150 were excited by 375 nm and executed at 555 nm, 521 nm, 503 nm, and 455 nm emission wavelengths respectively at room temperature (Figure 5).

Display full size

Figure 5. 

The time-resolved PL decay profiles of the GQDs 100, GQDs 120, GQDs 130 and GQDs 150

The double exponential PL decay curves of GQDs were well fitted by equation (1). where I(t) indicates intensity, τ₁ and τ₂ are the decay time constants, A₁ and A₂ refer to the weight coefficients of τ₁ and τ₂, respectively [13, 14]. Furthermore, the average lifetime (τ_avg) of the GQDs was calculated by equation (2).

Equation (1):

Equation (2):

As shown in Figure 5, the bi-exponential decay time can be subdivided into two emission states, e.g., the intrinsic state (fast decay) and the defect state (slow decay) [15, 16]. Compared with the intrinsic state, emission resulted from the defect state (e.g., oxygen-containing groups) usually displays a longer lifetime [15–18]. The fitting parameters of the GQDs FL decay are listed in Table 1. The shorter lifetime (τ₁) of 1.32–1.53 ns may attribute to the intrinsic state emission, while the longer lifetime (τ₂) of 4.89–7.17 ns may result from the defect state emission. τ₂ increased from 4.89 ns (GQDs 100), 6.30 ns (GQDs 120) to 6.93 ns (GQDs 130) and 7.17 ns for the GQDs 150. The average lifetimes of the GQDs 100, GQDs 120, GQDs 130, and GQDs 150 were found to be 3.8 ns, 5.1 ns, 6.2 ns, and 6.5 ns, respectively, which are clearly longer than those previously reported data (< 2.5 ns) [4]. Although little variation of τ₁ was found for the GQDs, distinct differences between τ₂ appeared, indicating τ_avg of the GQDs are dominated by the defect state emission (Figure 5F) [19, 20].

Biocompatibility of the GQDs 100, GQDs 120, GQDs 130, and GQDs 150 were tested using MDA-MB-231 cells. As shown in Figure 6A, cell viabilities of the GQDs 100 and GQDs 120 decreased dramatically with increasing CQDs concentration, and only ~50% of the cells still lived at a GQDs concentration of 0.5 mg/mL after 24 h. In comparison, the biocompatibility of the GQDs 130 and GQDs 150 was found to be much better, compared with that of the GQDs 100 and GQDs 120. Cell viability of the GQDs 130 and GQDs 150 was approaching 95% even at a high GQDs concentration of 1 mg/mL, suggesting the GQDs are ideal candidates for nanomedicine applications, e.g., drug/gene delivery and bio-imaging, etc. The huge differences in biological compatibility of the GQDs may derive from their different size and carbon composition, e.g., the ratio between the Csp² and Csp³. The cell viability data may suggest that amorphous carbon is more toxic than crystalline carbon (Csp²), although future work needs to be carried out to verify this idea. Furthermore, the GQDs 150 were introduced into the MDA-MB-231 cells for in vitro bioimaging, where the MDA-MB-231 cells were imaged using an LSM510 confocal laser scanning microscope (with an argon blue laser light at 488 nm and a 505 nm emission filter). As shown in Figure 6B, the GQDs 150 showed clear FL in MDA-MB-231, indicating the GQDs 150 are promising fluorescent agent. There are molecular dyes with similar properties/structures like pyrene are toxic [21], while other dyes suffer from bleaching [22]. From this perspective, the GQDs 130 and GQDs 150 are ideal candidates for nanomedicine applications (e.g., drug/gene delivery and bio-imaging, etc.), owing to their excellent biocompatibility and PL response.

Display full size

Figure 6. 

Biocompatibility of the GQDs. A. Cell viability of the GQDs 100, GQDs 120, GQDs 130, and GQDs 150 for 24 h; B. confocal FL images of GQDs 150 in MDA-MB-231 cells

Discussion

In the current study, GQDs were prepared using anthracite as a precursor. The GQDs 100, GQDs 120, GQDs 130, and GQDs 150 solutions were found to be orange-red, yellow-green, green, and blue under 365 nm excitation UV lamp, respectively. The XPS data suggests high temperature intensifies oxidation of the amorphous sp³ carbon, resulting in GQDs with higher crystalline structure (Csp²). Compared with the GQDs 100 and GQDs 120, the GQDs 130 and GQDs 150 showed much higher biocompatibility, which may attribute to their higher Csp² composition and smaller size. The results suggest the GQDs 130 and GQDs 150 are ideal candidates for nanomedicine applications, e.g., drug/gene delivery and bio-imaging, etc. Further work will focus on uncovering the mechanism between biocompatibility differences of the GQDs, whilst enhancing the PL intensity of the GQDs.